Composition wherein recycled cellulosic pulp is deinked

ABSTRACT

A composition containing an aqueous, recycled cellulosic fibre pulp, print pigments contaminating the pulp, from 0.1% to 10% based on the weight of the pulp solids of a curable precursor of a solid polymer resin which is not substantive to the cellulosic fibres of the pulp, and a catalyst capable of curing the resin precursor in the dispersion; wherein the resin precursor contains a mixture of a fluid prepolymer having at least two reactive functional groups per molecule and a cross-linking agent capable of reacting with the functional groups.

This application is a division, of application Ser. No. 731,527, filed May 7, 1985, now abandoned.

BACKGROUND

An increasingly large proportion of cellulosic pulp for the paper industry is produced from recycled waste cellulosic material, especially repulped newsprint and magazines. Pulp containing either of these wastes is normally contaminated with pigments derived from the ink, which must be removed in order to obtain adequate brightness.

Conventionally, particles of pigment are removed by froth flotation, using the surfactants naturally present in the pulp in order to promote foaming, or, less commonly, adding extraneous surfactants and/or foam boosters. An alternative is to use various solvents and/or surfactants to wash the pigment out of the pulp. Neither of these processes has proved capable of removing sufficient of the print to provide maximum realisable brightness.

In an attempt to improve the degree of separation of the print, various proposals have been made to agglomerate the print or adsorb it onto relatively large particles which will be more readily separated by flotation, or even by centrifugation or screening. All these proposals have, however, had serious drawbacks which have prevented their adoption commercially, despite the recognised inadequacy of the conventional washing and flotation technology.

THE PRIOR ART

FR 1,379,252 and U.S. Pat. No. 3,377,234 described the addition of surfactants to the pulping liquor prior to pulping. This approach does not result in complete separation of print. U.S. Pat. No. 4,013,505 and U.S. Pat. No. 4,147,616 describe the precipitation of calcium soap in the pulper to adsorb the print, followed by centrifugal separation of the resulting curds. This approach is only partially successful.

U.S. Pat. No. 3,846,227 and U.S. Pat. No. 3,963,560 describe the use of N-cyclohexyl pyrrolidone as solvent in the pulping stage, to promote removal of print. The process requires relatively high temperatures of about 73° C., which substantially increases the energy cost of the process, and causes unacceptable solvent losses.

GB No. 2,080,354 has proposed the addition of polymers to pulp at temperatures above their softening point in order to remove adhesives from recycled pulp. High temperatures are required, and efficient deinking is not alleged.

THE PROBLEM

Waste paper pulp is a chemically and physically complex system which is highly variable in an unpredictable manner. Little is known about the mechanism by which known deinking processes operate. The approach has hitherto been largely empirical.

We have therefore set out to discover the reasons for the inadequate performance of prior art processes.

By far, the major pigment present in repulped paper, and the one with the greatest effect on the final brightness, is carbon black, which is also one of the more intractable in its response to deinking processes. In the following discussion reference is specifically made to carbon black. The comments are, however, generally applicable to other pigments.

We believe, without wishing to be bound thereby, that carbon black is present in print, especially in newspapers, as particles weakly held in an oily matrix. During pulping we believe that this disintegrates, releasing small particles which lodge in the fibrillar surface of the fibres. We believe that the particles, once entrapped, are particularly difficult to remove by known deinking technology.

THE INVENTION

We have now discovered that substantially improved deinking can be obtained by pulping waste paper in an aqueous suspension of a non-fibre-substantive, room temperature vulcanisable resin, and curing the resin in situ. We believe that, in our invention, any pigment particles may become rapidly coated with uncured or partially cured resin, which inhibits disintegration and subsequent redeposition onto the cellulosic fibres, and which on curing, causes the particles to form agglomerates, which are relatively resistant to comminution and are separable from the pulp by conventional means such as washing, flotation, centrifugation or screening.

According to one embodiment, our invention provides an aqueous dispersion of at least one fluid, non-fibre-substantive resin precursor, curable in aqueous dispersion, and sufficient of a curing catalyst to effect curing of the composition, in the dispersion.

Preferably the composition contains a dispersant for the resin precursor. We have further discovered that the proportion of the curable resin required can be substantially reduced by admixing the composition with an inert extender or diluent, thereby improving the economics of the process.

According to a second embodiment, our invention therefore provides a composition comprising from 10 to 85% by weight thereof, of a fluid, non-fibre-substantive resin precursor, curable in aqueous dispersion, at least 5% by weight of the composition of an inert, non-fibre-substantive, fluid diluent and an effective amount of a dispersant for the composition.

According to a further embodiment, our invention provides a method of pulping recycled cellulosic material, contaminated with print, which comprises macerating the material in an aqueous dispersion containing sufficient of a fluid, non-fibre-substantive, resin precursor, curable in said dispersion, to facilitate subsequent deinking, and curing said resin precursor during said maceration.

THE RESIN PRECURSOR

The resin precursor according to our invention may be any non-fibre-substantive fluid which is curable in aqueous suspension, and preferably in aqueous alkaline suspension. In particular it is desirable that the precursor should be curable at temperatures below 50° C., preferably at room temperature. The resin precursor is preferably a sufficiently hydrophobic material not to be readily adsorbed onto the cellulosic fibres, but is desirably compatible with the print. Typically the resin precursor comprises a mixture of a fluid, prepolymer having at least two reactive functional groups per molecule and a cross linking agent able to react with the functional groups, at least in the presence of a suitable catalyst. Where the polymer system is capable of curing in the pulper, in the absence of a catalyst, the resin precursor will normally be formed in situ, the cross linking agent being added to the prepolymer on or shortly before addition to the pulper.

Most preferably, the resin is a room temperature vulcanisable organopolysiloxane. Particularly suitable are mixtures of a dihydroxy poly (dialkylsiloxane) polymer with a poly (alkylhydrosiloxane) cross-linking agent. Preferably, the alkyl groups in each case are lower (e.g. 1 to 4 carbon) alkyl groups, typically methyl groups. An alternative curable resin system for use according to the present invention comprises an oligomeric hydroxy acrylate prepolymer cross linked with a di isocyanate, e.g. a hydroxy ethyl acrylate resin mixed with 1,6-hexamethylene di isocyanate.

Typically the prepolymer has a mean molecular weight of from 5,000 to 70,000 preferably from 10,000 to 50,000 e.g. 30,000 to 45,000. We particularly prefer prepolymers comprising a wide spread of molecular weights e.g. a mixture of a short chain prepolymer M.W. 3,000 to 12,000 a long chain prepolymer M.W. 50,000 to 70,000.

The cross-linking agent typically has a mean molecular weight of from 1,000 to 5,000. Typically the cross-linking agent is present in a proportion of from 1:10 to 10:1; preferably from 1:2 to 2:1, most preferably 3:4 to 4:3 e.g. 1:1 by weight based on the difunctional polymer.

THE DISPERSANT

Any surfactant or dispersant which is water soluble or miscible and also miscible with the relatively hydrophobic resin precursor may be employed. Examples of dispersants for organo polysiloxane resin precursors are non-ionic surfactants such as polyalkoxylated organopolysiloxanes, e.g. a poly (dimethylsiloxane) poly (ethyleneglycol) ether, and poly ethoxylated sorbitan monoalkanoates, and cationic surfactants. Anionic surfactants are less preferred.

Particularly preferred, however are film forming dispersants and especially polymeric protective colloids such as polyvinyl alcohol, carboxymethylcellulose, polyvinylpyrrolidone or cellulose acetate.

The proportion of dispersant is sufficient to form a stable dispersion for the resin precursor in water. Amounts in excess of the minimum required to disperse the resin percursor are preferably avoided on economic grounds. Typically the dispersant is present in a proportion of from 0.1 to 20% by weight of the resin precursor, e.g. 3 to 7%. We do not exclude the possibility of dispersing the resin precursor without a dispersant, or using the dispersant action of normal components of the pulp adventitiously present in the pulper.

THE DILUENT

The diluent is optionally, present in any proportion up to about 95% by weight of the composition, preferably 5 to 90%, e.g. 55 to 80%, especially 65 to 75%.

The diluent may be any inert oil which is sufficiently hydrophobic to be non-fibre-substantive, and to be miscible with the resin precursor. Typical examples of diluents include polydimethylsiloxanes with terminal methyl groups and hydrocarbon oils. The diluent is preferably sufficiently fluid for the composition to be pourable, but sufficiently viscous to provide effective protection to particles of print in the pulp to prevent comminution and/or entrapment in the early stages of pulping and to ensure a mechanically strong cured agglomerate.

THE CATALYST

The catalyst may be any catalyst capable of catalysing the curing of the resin precursor in aqueous suspension, preferably at room temperature. Particularly preferred are organotin catalysts such as the dialkyltin dialkanoates. Preferably each of the two alkyl groups are lower alkyl groups having, for example, 2 to 4, preferably 4, carbon atoms and each of the two alkanoyl groups have from 2 to 20 carbon atoms, preferably 8 to 14, e.g. dibutyltin bis (ethylhexanoate) or dibutyltin dilaurate.

The activity and the volatility of the catalyst increase with decreasing carbon number of the alkanoyl groups. We prefer a catalyst which is sufficiently active to cure the resin precursor fully within the normal pulping period, e.g. 15 to 40 minutes. More active catalysts, e.g. dibutyltin diacetate, although operative are less preferred.

The catalyst may be used as a solution in an organic solvent such as trichlorethylene, but we prefer to use aqueous based emulsions of catalyst, which are commercially available and which have been found to give better activity in the aqueous pulping liquor.

In general we believe that the brightness of the pulp tends to reach a peak at the completion of the curing period and may thereafter decline if pulping is continued. We therefore prefer catalysts which give a curing time approximately equal to the pulping time rather than those which give substantially complete curing at an early stage in the pulping process.

We prefer to use a catalyst, even with systems which are capable of curing in the absence of a catalyst at the temperatures obtaining in the pulper, although it is not essential to our invention.

THE PULPING LIQUOR

Preferably the resin precursor is dispersed in water, in the presence of the catalyst (or of added cross linking agent, where no catalyst is required) and allowed to precure for a short period, e.g. 10 secs to 5 minutes, preferably 0.5 to 1 minutes and at a pH of preferably 8 to 12, before adding the waste. Typically the precure is from 1 to 10% of total curing time. Preferably the resin precursor is used in a proportion of 0.1 to 10% based on the weight of pulp solids, more preferably 1 to 5%, e.g. 1.5 to 4%.

The catalyst may be present in a proportion of from 0.1 to 50% based on the weight of resin precursor, preferably 0.5 to 20%, e.g. 1 to 10%.

The pulping liquor is preferably alkaline. Typically the pulper contents should have a pH of 8 to 12.5, e.g. 9 to 10. This may be achieved using for example sodium hydroxide, sodium carbonate, sodium silicate or mixtures thereof. The resin precursor and catalyst may be suspended directly in the pulping liquor, or alternatively a more concentrated suspension may be prepared and added to the pulping liquor shortly before pulping.

THE PULPING OPERATION

The furnish for the pulp may comprise newsprint and/or magazines and/or other ink contaminated cellulosic wastes. The furnish preferably comprises a mixture of newsprint and magazines, e.g. comprising 10 to 60% by weight of magazines. However the process is operable with 100% newsprint, a furnish that is particularly difficult to deink satisfactorily with existing technology. The waste is macerated with the pulping liquor for from 10 to 60 mins, preferably 15 to 40 mins, at temperature which may typically be in the range 5° to 60° C., preferably 20° to 50° C., e.g. 35° C. The pulp may contain from 2 to 25% solids more usually 5 to 15%.

SEQUESTRANTS

We have discovered that the brightness of pulp deinked according to our process is substantially enhanced by the presence in the pulping liquor of a sequestrant for alkaline earth metal and especially for calcium, e.g. ethylenediamine tetracetic acid; or phosphates, condensed phosphates or phosphonates, especially sodium tripolyphosphate, or silicates. This constitutes a preferred aspect of our invention. We prefer that the sequestrant should be present in amounts up to the stoichiometric amount based on the total sequesterable alkaline earth metal ion present in the pulp.

MISCELLANEOUS ADDITIVES

It is desirable that the cured resin particles should have a physical form such that they are readily separable from the pulp. For example they may differ substantially in density from the aqueous medium, preferably being substantially lighter, to facilitate centrifugal separation or they may be of a sufficient size to permit effective screening. The former may be achieved for example by selection of a low density extender, or by incorporating a blowing agent into the resin precursor. The latter may be a volatile liquid such as a fluorocarbon which is evaporated by the exothermic curing reaction to form expanded particles.

Alternatively, either the size or the density may be controlled by the addition of solid particles or granules of polymer. Preferably the particles are of a low density material such as expanded polystyrene and/or are of a sufficient size to be separable by screening. They preferably have a surface upon which the resin precursor and pigment will readily coagulate.

We have found in particular that separated coarse particles, either of an added polymer with print agglomerated on the surface, or of the cured agglomerated resin itself, can advantageously be recycled to the pulper in order to provide a more complete separation of the agglomerated print.

According to a further embodiment of our invention, therefore, recycled cellulosic material, contaminated with print, is repulped in a pulper in the presence of a dispersed curable resin which is non-substantive to the cellulose, but substantive to the print, in conditions adapted to effect curing of the resin and agglomeration of the print thereby; pulp is withdrawn from the pulper; cured resin is separated from the pulp; and a part of the cured resin is recycled to the pulper.

Surfactants, foam stabilizers or anti-foams may be added to the pulper, or subsequently, to promote or control foaming.

SEPARATION

The coagulated print may be separated from the pulp using any of the known procedures, depending upon the physical form of the cured particles.

The particles may be separated using conventional froth flotation. If necessary foam boosters and/or inhibitors may be added to the pulp to regulate the degree of foaming. Alternatively the agglomerated print may be removed by washing e.g. by dewatering and reslurrying the pulp.

If the particles differ sufficiently in density from the pulp they may be separated centrifugally, while sufficiently large particles may be separated by screening.

Typically, the pulp is diluted to a solids content of less than 2% by weight and screened to remove large particles. Any ink containing particles remaining in the pulp may then be separated by washing, centrifugation and/or flotation.

The invention will be illustrated by the following Examples:

Except where stated to the contrary, the examples used the following conditions:

Resin precursor:

50% by weight hydroxy-functional polydimethylsiloxane

45% by weight Si-H functional polydimethylsiloxane prepolymer

5% by weight polyethyleneoxy-/polypropyleneoxy-functional

polydimethylsiloxane.

Pulper consistency : 4%

Initial pulper pH : 10.5

Initial pulper temperature : 30° C.

Pulping time : 25 minutes.

Resin addition level : 2% on fibre by weight.

Method of addition : resin mixture added to water and dispersed prior to addition of fibre, caustic soda and catalyst.

Furnish : 100% newsprint.

EXAMPLE 1

Using 0.2%, by weight of fibre, of sodium dibutyltin dilaurate as catalyst in a laboratory test run, the ex-pulper brightness was 49% compared with 41% in the absence of resin.

EXAMPLE 2

Example 1 was repeated using 100% magazines in place of newsprint. Ex-pulper brightness was 57% compared with 54% in the absence of resin.

EXAMPLE 3

Example 1 was repeated using 50% by weight newsprint, 50% magazines as furnish. Ex-pulper brightness was 52% compared with 47% in the absence of resin.

EXAMPLES 4-6

Using 1.5%, by weight of fibre, of different catalysts results were:

No resin--45% brightness;

Example 4--dibutyltin diacetate 55.5% brightness;

Example 5--dibutyltin dilaurate 56.5% brightness;

Example 6---dibutyltin bis (2-ethylhexanoate) (in ethanol) 58% brightness.

EXAMPLE 7

FIG. 1 represents the variation in pulp brightness with time in a mill trial, using dibutyltin diacetate catalyst with 1 ton of newsprint, at a consistency of 12 to 15%. The lowest curve is a comparative run with no resin added. The middle curve is with 2% resin and 0.25% catalyst, based on the weight of fibre, and the highest curve is with 4% resin and 0.5% catalyst based on the weight of fibre.

EXAMPLE 8

FIG. 2 shows the effects of varying temperature on 6 experimental runs using 4% resin and 1.5% by weight dibutyltin diacetate based on the weight of fibre.

EXAMPLE 9

FIG. 3 shows the effect of increasing resin concentration using 1.5% by weight of dibutyltin diacetate based on the weight of fibre.

EXAMPLE 10

Example 1 was repeated adding expanded polystyrene beads of from 1 to 10 mm. diameter to the dispersed resin precursor immediately prior to the addition of the fibre. The beads were readily separated from the pulp and gave a substantial improvement in agglomeration and separation of the print. Optimum results were obtained with 1-2 mm beads. The separated beads were recycled to the pulper and the experiment repeated. The recycled beads provided a substantially equivalent improvement in the agglomeration of the print to that provided by the original uncontaminated beads.

EXAMPLE 11

Example 1 was repeated. Particles of agglomerated print were separated from the pulp and 50% of the separated particles were recycled to the pulper and the example repeated again. On the second run improved agglomeration and easier separation was observed.

EXAMPLES 12 and 13

An acrylic resin precursor was used in the Examples 12 and 13 consisting of

    ______________________________________                                         wt % Substance                                                                             Function  Carrier    Trade Mark                                    ______________________________________                                         65  hydroxyethyl-                                                                              prepolymer                                                                               50% in   "DURASOL"                                       acrylate              butylacetate                                                                            346                                         30  hexamethylene-                                                                             cross linker                                                                             xylene   "DESMODUR"                                      1,6-diisocyanate               N75                                         5   ethylene    dispersant         "GLYCOL B"                                      glycol/                                                                        propylene glycol                                                               hydroxymethyl                                                                  siloxane                                                                       copolymer                                                                  ______________________________________                                    

This was compared with the silicone resin precursor of Example 1 as follows:

EXAMPLE 12

    ______________________________________                                         Furnish    100% News                                                           Catalyst   Dibutyltindilaurate (1% on fibre addition)                          Brightness R.sub.457                                                                           Ex-pulper Infinite wash                                        ______________________________________                                         Caustic only    37        49                                                   3% Acrylate/caustic                                                                            45        511/2                                                2% Silicone/caustic                                                                            47        551/2                                                ______________________________________                                    

EXAMPLE 13

    ______________________________________                                         Furnish    50/50 News/magazines                                                Catalyst   Dibutyltindilaurate (1% on fibre addition)                          Brightness R.sub.457                                                                            Ex-pulper After flotation                                     ______________________________________                                         Caustic only     50        541/2                                               2% Acrylate RTV/caustic                                                                         52        631/2                                               2% Silicone RTV/caustic                                                                         56        62                                                  ______________________________________                                    

EXAMPLE 14

To illustrate the effects of including a non-functional extender in the resin example 1 was repeated adding various proportions of methyl functional polydimethyl siloxane to the reactive prepolymer, with the following results:

    ______________________________________                                         % by wt. reactive prepolymer                                                                      Ex pulper brightness                                        ______________________________________                                         95                 51.5                                                        45                 51.8                                                        25                 51.9                                                        10                 50.0                                                        Comparative (no resin)                                                                            40.7                                                        ______________________________________                                    

EXAMPLE 15

A prepolymer emulsion was prepared comprising:

Dihydroxy poly(dimethyl siloxane) n=49-144; (mean MW=7566) 10 g

Dihydroxy poly(dimethyl siloxane) n=850; (mean MW=63066) 40 g

Poly(methyl hydrosiloxane) n=40; (mean MW=2562) 45 g

5% aqueous solution of polyvinyl alcohol; 165 g

A catalyst emulsion having 33% by wt. of solids was prepared separately containing:

    ______________________________________                                         dibutyl tin dilaurate   60 g                                                   polyvinyl alcohol       7 g                                                    water                   133 g                                                  ______________________________________                                    

1900 ml of water and 6 g prepolymer emulsion (1% resin based on the weight of fibre) were stirred in a pulper with 13 ml concentrated sodium hydroxide solution and 0.3 ml of the catalyst emulsion (0.05% based on the weight of fibre) at room temperature for a 30 second precure period. 2.36 gm of waste newsprint were then added to provide a pulp having a consistency of 11%.

After 25 minutes pulping the pulp was washed and compared with a control run using sodium hydroxide solution only.

    ______________________________________                                                 Ex pulper brightness                                                                        Washed brightness                                         ______________________________________                                         Control   36.5           42.8                                                  Example 15                                                                               46.3           51                                                    ______________________________________                                     

We claim:
 1. A composition comprising:(i) an aqueous, recycled cellulosic fibre pulp; (ii) print pigments contaminating said pulp; (iii) dispersed in said contaminated pulp, from 0.1% to 10% based on the weight of the pulp solids of a curable precursor of a solid polymer resin which is not substantive to the cellulosic fibres of said pulp; and (iv) a catalyst capable of curing said precursor in said dispersion; wherein(a) said resin precursor consists essentially of a mixture of a fluid prepolymer having at least two reactive functional groups per molecule and a cross-linking agent capable of reacting with said functional groups; (b) said catalyst is present in an amount effective to cure said resin precursor in said dispersion and thereby to form agglomerates comprising cured resin and at least some of said contaminating pigment; and (c) said agglomerates can be separated from said dispersion to effect deinking of said pulp.
 2. The composition of claim 1 additionally containing an amount of a dispersant for the resin precursor effective to disperse said resin precursor in said composition.
 3. The composition of claim 2 wherein said resin precursor is curable at temperatures below 50° C.
 4. The composition of claim 3 wherein said resin precursor consists essentially of dihydroxypoly(dialkylsiloxane) polymer with a poly(alkylhydrosiloxane) cross-linking agent.
 5. The composition of claim 4 wherein each alkyl group of said resin precursor has from 1 to 4 carbon atoms.
 6. The composition of claim 5 wherein said alkyl groups are methyl groups.
 7. The composition of claim 3 wherein said resin precursor is curable at room temperature.
 8. The composition of claim 3 wherein said resin precursor consists essentially of an oligomeric hydroxy acrylate prepolymer and a diisocyanate cross-linking agent.
 9. The composition of claim 2 wherein the dispersant is selected from the group consisting of polyvinyl alcohol, polyvinyl pyrrolidone, carboxymethyl cellulose and cellulose acetate.
 10. The composition of claim 2 wherein the dispersant is present in an amount of from 0.1-20% by weight of said resin precursor.
 11. The composition of claim 1 additionally containing a diluent for said resin precursor, said diluent being an inert, non-fibre-substantive fluid and said resin precursor and said diluent being present in amounts of, respectively, from 10 to 85% by weight and at least 5% by weight of the dispersed materials.
 12. The composition of claim 11 wherein said diluent is present in an amount of from 55 to 80% by weight of the dispersed materials.
 13. The composition of claim 11 wherein said diluent is a polydimethyl siloxane with terminal methyl groups.
 14. The composition of claim 11 wherein said diluent is a hydrocarbon oil.
 15. The composition of claim 1 wherein said curing catalyst is a dialkyltin dialkanoate.
 16. The composition of claim 15 wherein said catalyst is a dibutyltin dialkanoate wherein each alkanoate moiety has from 8 to 14 carbon atoms.
 17. The composition of claim 15 wherein said catalyst is present in an amount of from 0.1-50% based on the weight of said resin precursor.
 18. The composition of claim 1 wherein said cross-linking agent is present in a proportion of from 1:10 to 10:1 by weight based on the prepolymer.
 19. The composition of claim 1 having a pH of from 8 to 12.5.
 20. The composition of claim 1 additionally containing a sequestrant for any calcium ions. 